Annealing and Stress Relief at ThermoFusion
Annealing and Stress Relief at ThermoFusion
Annealing and Stress Relief
Annealing and Stress Relief are terms used to describe heating a part to a certain temperature, holding it at that temperature, and then cooling the part at a relatively slow rate. Think of it this way: You’re stressed from a long day at work (the heat treat term is “work hardened”). You need to relieve the stress. Sitting in the easy chair and relaxing, that would be stress relief. But once you get up, there’s still the nagging pain in your back/leg/shoulder.
Annealing gets rid of a lot more stress than a simple stress relief, and in many cases actually causes a softening of the material. You could say its equivalent to soaking in the hot tub or spa for awhile, then having a nice massage. A lot more of the nagging pain is gone.
So, stress relief is a lower-temperature heat treating process that relieves some of the residual stresses, and cools the parts slowly so no new stresses are introduced. Annealing, on the other hand, is a higher temperature heat treating process that relieves a lot more stress and also softens the material.
All metals and steels can be stressed, which means that all can be stress relieved. Many also get too hard, usually through too much stress, and can be softened. Plastic is the latest material that we’re annealing to relieve molding stresses
Annealing gets rid of a lot more stress than a simple stress relief, and in many cases actually causes a softening of the material. You could say its equivalent to soaking in the hot tub or spa for awhile, then having a nice massage. A lot more of the nagging pain is gone.
So, stress relief is a lower-temperature heat treating process that relieves some of the residual stresses, and cools the parts slowly so no new stresses are introduced. Annealing, on the other hand, is a higher temperature heat treating process that relieves a lot more stress and also softens the material.
All metals and steels can be stressed, which means that all can be stress relieved. Many also get too hard, usually through too much stress, and can be softened. Plastic is the latest material that we’re annealing to relieve molding stresses
Thursday, June 25, 2015
పాత నోట్ల చలామణి గడువుడి సెంబర్‌ 31 వరకు పొడిగింపు
పాత నోట్ల చలామణి గడువుడి సెంబర్‌ 31 వరకు పొడిగింపు2015ముంబై : 2005కు ముందు ముద్రించిన పాత కరెన్సీ నోట్ల చలామణిని రిజర్వు బ్యాంకు ఈ సంవత్సరం డిసెంబర్‌ 31 వరకు పొడిగించింది. ఇలా గడువు పొడిగించడం ఇది వరసగా మూడో సారి. నిజానికి ఈ నెలాఖరులోగానే ఈ నోట్లు ఉన్న వ్యక్తులు, సంస్థలు వాటిని తమ బ్యాంకు ఖాతాల్లో డిపాజిట్‌ చేయడం లేదా సమీపంలోని బ్యాంకుల శాఖల్లో మార్చుకోవడం చేయాలని ఆర్‌బిఐ ఇంత కు ముందు కోరింది. ఇంతలోనే మళ్లీ ఈ నోట్ల చలామణిని మరో ఆరు నెలలు పొడిగిస్తున్నట్లు తెలిపింది. సరైన భద్రతా అంశాలు లేకపోవడంతో 2005కు ముద్రించిన కరెన్సీ నోట్లను పోలిన దొంగ నోట్లు ఎక్కువగా చలామణిలోకి రావడంతో వీటిని చలామణి నుంచి పూర్తిగా ఉపసంహరించాలని నిర్ణయించిది. 2005 నాటి మహాత్మా గాంధీ సీరిస్‌లో ముద్రించిన రూ.100 నోట్లలో సైతం మరిన్ని భద్రతా అంశాలు జోడించాలని కూడా ఆర్‌బిఐ నిర్ణయించింది.
Tuesday, June 23, 2015
Monday, June 22, 2015
Sunday, June 21, 2015
Subscribe to:
Posts (Atom)